Rajagukguk, Juniastel (2019) Comparative investigations of gadolinium based borate glasses doped with Dy3+ for white light generations. Solid State Sciences, 89. pp. 50-56. ISSN 1293-2558
full text.pdf - Published Version
Download (4MB) | Preview
Abstract
Gadolinium-based borate glasses doped with Dy3+ ions were developed by melt quenching technique for white light generation. The title glasses were examined by XRD, optical absorption spectra and Photoluminescence spectra. From photoluminescence emission spectra, the higher intensity peak was observed at 575 nm (4F9/2 → 6H13/2) for present glass samples. The experimental decay rate (τexp) of 4F9/2 transition of Dy3+ ions were found to be a decline in increasing of Dy2O3 content. The Inokuti-Hirayama (IH) model is used to explain the non-exponential decay time by putting S = 6, which confirmed that the energy is transfer through cross-relaxation is of dipole–dipole nature among the Dy2O3. The values of color coordinates match with the range of white light of chromaticity (CIE) diagram. The color chromaticity coordinates (u, v) and color correlated temperature (CCT) values for present glasses were correlated with standards, which are closely related to the standard, therefore, the prepared glasses might be helpful for different photonic applications such as white LEDs.
Item Type: | Article |
---|---|
Keywords: | Gadolinium;Borate;Glasses;Spectra;Luminescence |
Subjects: | Q Science > QC Physics Q Science > QC Physics > QC120 Descriptive and Experimental mechanics Q Science > QC Physics > QC350 Optics. Light Q Science > QD Chemistry > QD450 Physical and theoretical chemistry |
Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam |
Depositing User: | Mrs Catur Dedek Khadijah |
Date Deposited: | 30 Dec 2020 06:54 |
Last Modified: | 30 Dec 2020 06:54 |
URI: | https://digilib.unimed.ac.id/id/eprint/41056 |